Acrylate and methacrylate terminated polydiene macromolecular monomers having a substantially uniform molecular weight distribution

ABSTRACT

This application discloses a copolymerizable macromolecular monomer having a substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not substantially above about 1.1, wherein Mw is the weight average molecular weight of the macromolecular monomer, and Mn is the number average molecular weight of the macromolecular monomer, said macromolecular monomer being represented by the structural formula: WHEREIN R is lower alkyl and R&#39;&#39; and R&#39;&#39;&#39;&#39; are each either hydrogen or methyl, and n is a positive integer having a value of at least about 20.

United States Patent Milkovich et al.

[ Jan. 21, 1975 ACRYLATE AND METIIACRYLATE TERMINATED POLYDIENE MACROMOLECULAR MONOMERS HAVING A SUBST-ANTIALLY UNIFORM MOLECULAR WEIGHT DISTRIBUTION inventors: Ralph Milkovich, Naperville;

Mutong T. Chiang, Palos Heights,

both of I11,

Assignee: CPC International Inc., Englewood Cliffs, NJ.

Filed: July 2, 1973 Appl. No.: 376,030

Related US. Application Data Division of Ser. No. 282,099, Aug. 21, 1972, Pat. No. 3,786,l 16, Continuation-in-part of Ser. No. 244,205, April14', 1972, which is a continuation-in-part of Ser. No. 117,733, Feb. 22, 1971, abandoned.

US. Cl 260/94.7 A, 260/82.l, 260/882 S,

260/935, 260/942 M, 260/878, 260/879 Int. Cl. C08d l/20, C08d 5/04 Field of Search 260/947 A References Cited UNITED STATES PATENTS 10/1971 Kumanotani et al. 260/78.4 D X 3,639,519 2/1972 Hsieh et al 260/9417 A X 3,652,520 3/1972 Ryan et al 260/947 A X 3,699,186 10/1972 Schrage et al. 260/947 A X 3,705,866 12/1972 Shibato et al 260/784 D X Primary Examiner-William F. Hamrock Attorney, Agent, or Firm-Albert P. Halluin [57] ABSTRACT wherein R is lower alkyl and R and R" are each either hydrogen or methyl, and n is a positive integer having a value of at least about 20.

10 Claims, No Drawings ACRYLATE AND METHACRYLATE TERMINATED POLYDIENE MACROMOLECULAR MONOMERS HAVING A SUBSTANTIALLY UNIFORM MOLECULAR WEIGHT DISTRIBUTION CROSS-REFERENCE TO'RELATED APPLICATIONS This application is a division of co-pending application Ser. No. 282,099, filed Aug. 21, 1972, now US. Pat. No. 3,786,116, issued Jan-15, 1974. Application Ser. No. 282,099 is a continuation-in-part of copendingapplication Ser. No. 244,205, filed Apr. 14, 1972, which in turn is a continuation-in-part of application Ser. No. 117,733, filed Feb. 22, 1971, now abancloned.

BACKGROUND OF THE INVENTION 1. Statement Of The Invention The present invention relates to chemically joined,.

phase separated thermoplastic graft copolymers and novel macromolecular monomers useful in the preparation of the graft copolymers.

The copolymerizable macromolecular monomers of the present invention have a substantially uniform molecular weight distribution such that their ratio of Mw/Mn is not substantially above about 1.1, wherein Mw is the weight average molecular weight of the macromolecular monomer, and Mn is the number average molecular weight of the macromolecular monomer, said macromolecular monomer being represented by the structural formula ties of polyolefins and other polymers by either chemical or mechanical means generally has resulted in a sacrifice of many of the beneficial properties of both the polyolefin and the additional polymer. For example, graft copolymers of polyethylene and polypropylene have been prepared only with difficulty due to the inous solvent systems, particularly when containing a' rubbery, amorphous component.

The above considerations recognized by those skilled in the art with respect to the incompatability of polyolefins with other polymers find almost equal applicability in the case of other plastics such as the polyacrylates, polymethacrylates, polyvinylchlorides, etc. Thus, the incompatability of both natural and synthetic polymers becomes increasingly apparent as more and more polymers having particularly good properties for special uses have become available, and as efforts have been made to combine pairs of these polymers for the purpose of incorporating the different, good properties of each polymer into one product. More often than not, these efforts have been unsuccessful because the resulting blends have exhibited an instability, and in many cases the desirable properties of the new polymers were R CH;-- C CH CH CHgCHgOi (I CH;

wherein R is lower alkyl and R and R" are each either hydrogen or methyl, and n is a positive integer having a value of at least about 20.

2. Description Of The Prior Art Polymer technology has developed to a high degree of sophistication and extensive research efforts in this direction are being undertaken to obtain improvements in polymer properties. Some of these efforts lead to polymer materials capable of competing with metals and ceramics in engineering applications. Generally, it is a requirement that these polymers be crystalline, since crystalline polymers are strong, tough, stiff and generally more resistant to solvents and chemicals that their non-crystalline counterparts.

Many poly alpha-olefins are crystalline and have excellent structural integrity; and, accordingly, have acquired increasing commerical acceptance as materials uses of polyethylene have also been limited due to its a Rll completely lost. As a specific example, polyethylene is incompatible with polystyrene and a blend of the two has poorer physical properties than either of the homopolymers. These failures were at first attributed to inadequate mixing procedures, but eventually it was concluded that failures were due simply to the inherent incompatibilities. Although it is now believed that this is a correct explanation, the general nature of such in- Despite the general acceptance of the fact of incompatibility of polymer pairs, there is much interest in devising means whereby the advantageous properties of combinations of polymers may be combined into one product.

One way in which this objective has been sought involves the preparation of block or graft copolymers. In this way, two different polymeric segments, normally incompatible with one another, are joined together chemically to give a sort forced compatibility. In such a copolymer, each polymer segment continues to manifest its independent polymer properties. Thus, the block or graft copolymer in many instances possesses a combination of properties not normally found in a homopolymer or a random copolymer.

Recently, U.S. Pat. No. 3,235,626 to -Waack, assigned to Dow Chemical Company, described a method for preparing graft copolymers of controlled branch configuration. It is described that the graft copolymers are prepared by first preparing a prepolymer by reacting a vinyl metal compound with an olefinic monomer to-obtain a vinyl terminated prepolymer. After protonation and catalyst removal, the prepolymer is dissolved in an inert solvent with a polymerization catalyst and is thereafter reacted with either a different polymer hava ing a reactive vinyl group or a different vinyl monomer under free-radical conditions.

The current limitations on the preparation of these copolymers are mechanistic. Thus, there is no means for controlling the spacing of the sidechains along the backbone chain and the possibility of the sidechains having irregular sizes. Due to the mechanistic limitations of the prior art methods, i.e., the use of an alpha olefin terminated prepolymer with acrylonitrile or an acrylate monomer, complicated mixtures of free homopolymers result.

In view of the above considerations, it would be highly desirable to devise a means for preparing graft copolymers wherein the production of complicated mixtures of free homopolymers is minimized and the beneficial properties ofthe sidechain and backbone polymer are combined in one product.

Moreover, it is recognized and documented in the literature, such as R. Waach et al, Polymer, Vol. 2, pp. 365-366 (1961), and R. Waach et al., J. Org. Chem.,

Vol. 32, pp. 3395-3399 (1967), that vinyl lithium is one of the slowest anionic polymerization initiators. The slow initiator characteristic of vinyl lithium when used to polymerize styrene produces a polymer having a broad molecular weight distribution due to the ratio of the overall rate of propagation of the styryl anion to that of the vinyllithium initiation. In other words, the molecular weight distribution of the polymer produced will be determined by the effective reactivity of the initiator compared withthat of the propagating anionic polymer species, i.e., vinyl lithium initiator reactivity compared to the styryl anion. Accordingly, following the practice of U.S. Pat. No. 3,235,626, a graft copolymer having sidechains of uniform molecular weight cannot be prepared.

U.S. Pat. Nos. 3,390,206 and 3,514,500 describe processes for terminating free-radical and ionic poly- SUMMARY OF THE INVENTION The present invention relates to thermoplastic graft copolymers comprised of copolymeric backbones containing a plurality of uninterrupted repeating-units of the backbone polymer and at least one integrally copolymerized moiety per backbone polymer chain having chemically bonded thereto a substantially linear polymer which forms a copolymerized sidechain to the backbone, wherein each of the polymeric sidechains has substantiallyfthe same molecular weight and each 4 polymeric sidechain is chemically bonded to only one backbone polymer.

The graft copolymers of the present invention assume a T" type structure when only one sidechain is copolymerized into the copolymeric backbone. However, when more than one sidechain is copolymerized into the'backbone polymer, the graft copolymer may be characterized as having a comb-type structure illustrated in the following manner:

wherein a represents a substantially linear, uniform molecular weight polymer or copolymer having a sufficient molecular weightsuch that the physical properties of at least one of the substantially linear polymers are manifest; b represents a reacted and polymerized end group chemically bonded to the sidechain, a, which is integrally polymerized into the backbone polymer, and c.is-the backbone polymer having uninterrupted segments of sufficient molecular weight such that the physical properties of the polymer are manifest.

The backbone of the graft copolymers of the present invention preferably contains atleast about 20 uninterrupted recurring monomeric units in each segment. It has been found that this condition provides the graft copolymer the properties of the polymer. In other words, the presence of segments containing at least about 20 uninterrupted recurring monomeric units provides the graft copolymers with the physical properties attributed to this polymer, such as crystalline melting point (Tm) and structural integrity.

The backbone polymeric segments of the chemically joined, phase separated thermoplastic graftcopolymers of the present invention are derived from copolymerizable monomers, preferably the low molecular weight monomers. These copolymerizable monomers include polycarboxylic acids, their anhydrides and amides, polyisocyanates, organic epoxides, including the thioepoxides, urea-formaldehyde, siloxanes, and ethylenically unsaturated monomers. A particularly preferred group of copolymerizable monomers include the ethylenically-unsaturated monomers, especially the monomeric vinylidene type compounds, i.e., monomers containing at least one vinylidene CH C-- group.

The vinyl type compounds represented by the formula wherein a hydrogen is attached to one of the free vamerizable end groups of 'the sidechain prepolymer under free-radical, ionic, condensation, or coordination (Ziegler or Ziegler-Natta catalysis) polymerization reactions. As it will be seen from the description of macromolecular monomers, described hereinbelow, the choice of polymerizable end groups includes any polymerizable compound commercially available Accordingly, the choice of respective polymerizable end group and copolymerizable monomer can be chosen, based upon relative reactivity ratios under the respective copolymerization reaction conditions suitable for copolymerization reaction. For example, alpha-olefins copolymerize with one another using Ziegler catalysts, and acrylates copolymerize with vinyl chloride, acrylonitrile and other alkyl acrylates. Accordingly, an alphaolefin terminated macromolecular monomer copolymerizes with ethylene and alpha-olefins using a Ziegler catalyst and an acrylate or methacrylate terminated macromolecular monomer copolymerizes with vinyl chloride, acrylonitrile, acrylates and methacrylates under free-radical conditions in a manner governed by the respective reactivity ratios for the comonomers.

As will be explained hereinafter, the excellent combination of beneficial properties possessed by the graft copolymers of the present invention are attributed to the large segments of uninterrupted copolymeric backbones and the integrally copolymerized linear sidechains of controlled molecular weight and narrow molecular weight distribution.

The term linear, referred to hereinabove, is being used in its conventional sense, to pertain to a polymeric backbone that is free from cross-linking.

The sidechain polymers having substantially uniform molecular weight are comprised of substantially linear polymers and copolymers produced by anionic polymerization of any anionically polymerizable monomer, as will be described hereinafter. Preferably, the sidechain polymer will be different from the backbone polymer.

It is preferred that at least one segment of the sidechain polymer of the graft copolymers of the present invention have a molecular weight sufficient to manifest the beneficial properties of the respective polymer. In other words, physical properties of the sidechain polymer such as the glass transition temperature (Tg) will be manifest. Generally, as known in the art, the average molecular weight of the segment of the polymeric sidechains necessary to establish the physical properties of the polymer will be from about 5,000 to about 50,000.

In light of the unusual and improved physical properties possessed by the thermoplastic graft copolymers of the present invention, it is believed that the monofunctionally bonded polymeric sidechains having substantially uniform molecular weight form what is known as domains".

STATEMENT OF THE INVENTION Briefly, the chemically joined, phase separated thermoplastic graft copolymers of the present invention are prepared by first preparing the sidechains in the form of monofunctional living polymers of substantially uniform molecular weight. The living polymers are thereafter terminated, as by reaction with a halogencontaining compound that also contains a reactive polymerizable group, suchas, for example, a polymerizable olefinic or epoxy group, or a compound which contains a reactive site to an anion of the living polymer and a polymerizable moiety which does not preferentially react with the anion, e.g., maleic anhydride. The monofunctional terminated living polymer chains are then polymerized, together with the backbone monomer, to form a chemically joined, phase separated thermoplastic graft copolymer wherein the polymeric sidechains are integrally polymerized into the backbone polymer.

DESCRIPTION OF THE PREFERRED EMBODIMENTS The chemically joined, phase separated thermoplastic graft copolymers derived from ethylenically unsaturated monomers as the backbone comonomer generally correspond to the following structural formula:

wherein R and R are each selected from the group consisting of hydrogen, lower alkyl, cycloalkyl, and aryl radicals; X and X are each selected from the group consisting of hydrogen, alkylene radicals (i.e., -[-CH ,x is a positive integer wherein the terminal methylene group in X is X hydrogen, lower alkyl, e.g., methyl, halogen, etc., and in the case of X, joins the backbone polymer with the sidechain polymer), a saturated ester (i.e.,

0 ll u C -OR or 0 --C-R wherein R is alkyl or aryl), nitrile (i.e., -C N), amide (i.e.,

\RII

wherein R and R are either hydrogen, alkyl or aryl radicals), amine (i.e.,

wherein R and R" are either hydrogen, alkyl or aryl radicals), isocyanate, halogen (i.e., F, Cl, Br or I) and ether (i.e.,O-R, wherein R is either alkyl or aryl radicals); X and X may be the same or different. However, in the case where X is an ester, X should be a functional group such as ester, halogen, nitrile, etc., as explained hereinabove with respect to the respective reactivity ratios of the comonomers used to prepare the graft copolymers; Y is a substantially linear polymer or copolymer wherein at least one segment of the polymer has a sufficient molecular weight to manifest the properties of the respective polymer, i.e., a molecular weight of from about 5,000 to about 50,000, preferably a molecular weight of from about 10,000 to about 35,000, more preferably 12,000 to about 25,000; the symbols a, b and c are positive integers, with the proviso that a and b are each a value such that the physical properties of the uninterrupted segments in the backbone, e.g., Tm, are manifest, preferably at least about 20; and the symbol 0 is at least one, but preferably greater than one, e.g., a value such that the molecular weight of the graft copolymer will be up to about 2,000,000.

The formation of the graft copolymers of the present invention may be better understood by reference to the following reactions illustrated by the equations set forth below wherein the invention is illustrated in terms of polystyrene sidechains and polyethylene backbones. The same principles, however, apply in case of the present invention wherein the sidechains are formed from conjugated dienes, such as butadiene or isoprene monomer segments. It can be seen from these equations that the first reactions involve the preparation of living polymers of polystyrene. The living polymers are 20 thereafter reacted with a molar equivalent of allyl chloride, wherein the reaction takes place at the carbonchloride bond, rather than at the carbon-carbon double bond. The vinyl terminated polystyrene, referred to herein as the alpha-olefin terminated macromolecular monomer, is then copolymerized with ethylene to produce a graft copolymer of polyethylene, whereby the vinyl moiety of the polystyrene is integrally polymerized into the linear polyethylene backbone.

Alternatively, the living polymer can be reacted with an epoxide such as, for example, ethylene oxide, to produce an alkoxide ion which can then be reacted with the halogen-containing olefin, i.e., allyl chloride, to produce an alpha-olefin terminated macromolecular monomer.

in the equations above, the symbols a, b, c, n and X are positive integers wherein a and b are at least about 20, n has a value of from about 50 to about 500, and x has a value corresponding approximately to the sum ofa and b.

FORMATION OF THE CRAFT COPOLYMER 0F ALPHA-OLEFIN TERMINATED POLYSTYRENE SIDECHAIN AND POLYETHYLENE BACKBONE Initiation: CH CH (CH )CHL:L cs a i 9 e 3H CH (CH )CHCH CH Li Propagationz (n-1)CH CH P 6 CH CH (CH )CHCH CH CH CH Li Termination with Active End Group: CH CHCH Cl CH CH (CH )C CH CH CH CH CH LiCl Graft Co 01 etization: xCH CH Polymerization Catalyst:

F v H 11 CH CH LCH CW% \A a fit b CH CH (CH );GH CH CH PREPARATION OF THE LIVING POLYMERS The sidechains of the chemically joined, phase separated graft copolymers, above, are preferably prepared by the anionic polymerization of a polymerizable monomer or combination of monomers. In most instances, such monomers are those having an olefinic group, such as the vinyl containing compounds, although the olefinic containing monomers may be used in combination with epoxy or thioepoxy containing compounds. The living polymers are conveniently prepared by contacting the monomer with an alkali metal hydrocarbon or alkoxide salts in the presence of an inert organic diluent which does not participate in or interfere with the polymerization reaction.

Those monomers susceptible to anionic polymeriza tion according to the present invention dienes including isoprene and butacliene. The preferred monomers are conjugated dienes containing 4 to 12 carbon atoms per molecule.

The initiators for these anionic polymerizations are any alkali metal hydrocarbons and alkoxide salts which Molecular weight 0 dropwise addition serves to destroy contaminants and thus permits better control of the polymerization.

To prepare a polymer of 'narrow molecular weight distribution, it is generally preferred'to introduce all of the reactive species into the system at the same time. By this technique, polymer growth by consecutive addition of monomer takes place at the same rate to an active terminal group, without chain transfer or termination reaction. When this is accomplished, the molecular weight of the polymer is controlled by the ratio of monomer to initiator, as seen from the following representation:

Living Polymer produce a monofunctional living polymer, i.e., only one end of the polymer contains a reactive anion. Those catalysts found suitable include the hydrocarbons of lithium, sodium or potassium as represented by the formula RMe wherein Me is an alkali metal such as sodium, lithium or potassium and R represents a hydro carbon radical, for example, an alkyl radical containing up to about 20 carbon atoms or more, and preferably up to about eight carbon atoms, an aryl radical, an alkaryl radical or an aralkyl radical. Illustrative alkali metal hydrocarbons include ethyl sodium n-propyl sodium n-butyl potassium, n-octyl potassium phen'yl sodium, ethyl lithium, sec-butyl lithium, t-butyl lithium and 2-ethylhexyl lithium. Sec-butyl lithium is the preferred initiator because it has a fast initiation which is important in preparing polymers of narrow molecular weight distribution.

The alkali metal hydrocarbons and are either available commercially or may be prepared by known methods, such as by the reaction of a halohydrocarbon, halobenzene and the appropriate alkali metal.

An inert solvent generally is used to facilitate heat transfer and adequate mixing ofinitiator and monomer. Hydrocarbons and ethers are the preferred solvents. Solvents useful in the anionic polymerization process include the aromatic hydrocarbons such as benzene, toluene, xylene, ethylbenzene, t-butylbenzene, etc. Also suitable are the saturated aliphatic and cycloaliphatic hydrocarbons such as n-hexane, n-heptane, noctane, cyclohexane and the like. In addition, aliphatic and cyclic ether solvents can be used, for example, dimethyl ether, diethyl ether, dibutyl ether, tetrahydrofuran, dioxane, anisole, tetrahydropyran, diglyme,

glyme, etc. The rates of polymerization are faster in the ether solvents than in the hydrocarbon solvents, and small amounts of ether in the hydrocarbon solvent increase the rates of polymerization.

The amount of initiator is an important factor in anionic polymerization because it determines the molecu- Holes of Monomer Moles of Initiator As it can be seen from the above formula, high concentrations of initiator leads to the formation of low molecular weight polymers, whereas, low concentrations of initiator leads to the production of high molecular weight polymers. 7

The concentration of the monomer charged to the reaction vessel can vary widely, and is limited by the ability of the reaction equipment to dissipate the heat of polymerization and to properly mix the resulting viscous solutions of the living polymer. Concentrations of monomer as high as 50% by weight or higher based on the weight of the reaction mixture can be used. How ever, the preferred monomer concentration is from about 5 to about 25% in order to achieve adequate mixmg.

As can be seen from the formula above and the foregoing limitations on the concentration of the monomer, the initiator concentration is critical, but may be varied according to the desired molecular weight of the living polymer and the relative concentration of. the monomer. Generally, the initiator concentration can range from about 0.001 to about 0.1 mole of active alkali metal per mole of monomer, or higher. Preferably, the concentration of the initiator will be from about 0.01 to about 0.004 mole of active alkali metal per mole of monomer.

The temperature of the polymerization will depend on the monomer. Generally, the reaction can be carried out at temperatures ranging from about l00C up to about C. When using aliphatic and hydrocarbon diluents, the preferred temperature range is from about -l0C to about 100C. With ethers as the solvent, the preferred temperature range is from about -l00C to about 100C. The polymerization of the styrene is generally carried out at slightly above room temperature.

The preparation of the living polymer can be carried out by adding a solution of the alkali metal hydrocar bon initiator in an inert organic solvent to a mixture of monomer and diluent at the desired polymerization temperature and allowing the mixture to stand with or without agitation until the polymerization is completed. An alternative procedure is to add monomer to a solution of the catalyst in the diluent at the desired polymerization temperature at the same ratethat it is being polymerized. By either method the monomer is converted quantitatively to a living polymer as long asthe system remains free of impurities which inactivate the anionic species. As pointed out above, however, it is important to add all of the reactive ingredients together rapidly to insure the formation of a uniform molecular weight distribution of the polymer.

The anionic polymerization must be carried out under carefully controlled conditions, so as to exclude substances which destroy the catalytic effect of the catalyst or initiator. For example, such impurities as water, oxygen, carbon monoxide, carbon dioxide, and the like. Thus, the polymerizations are generally carried out in dry equipment, using anhydrous reactants, and

,under an inert gas atmosphere, such as nitrogen, he-

permeation chromatogram of commercial polystyrene (Dow 666u) prepared by free-radical polymerization and polystyrene produced by the anionic polymerization process utilized in accordance with the practice of the present invention.

I PRODUCTION OF THE MACROMOLECULAR MONOMERS BY TERMINATION OF THE LIVING POLYMERS Living Polymer R CH C CH QQEEEEEQSL R CH2 CH Terminating Agent lium, argon, methane, and the like.

The above-described living polymers are susceptible to further reactions including further polymerization. Thus, if additional monomer, such as another different anionically polymerizable monomer such as ethylene oxide, is added the above-described living polymer initiates the polymerization of the ethylene oxide and the ultimate living polymer which results consists of a polybutadiene segment and a polyoxyethylene segment.

As noted above, the living polymers employed in the present invention are characterized by relatively uniform molecular weight, i.e., the distribution of molecular weights of the mixture of living polymers produced is quite narrow. This is in marked contrast to the typical polymer, where the molecular weight distribution is quite broad. The difference in molecular weight distribution is particularly evident from an analysis of the gel (9 CH CH Cl CH CI 9 Li n R H L Hz-CH 6 9 CH CH CH O Li O X g C CH;

CHzCHzOE C CH2 In the above equations, R, R, and R are each selected from the group consisting of hydrogen and lower alkyl, and aryl radicals. Preferably, R will be lower alkyl, such as sec-butyl; R will be either hydrogen or methyl; and R will be either hydrogen or lower alkyl radical. The symbol n is a positive integer such that the properties of the polymer are manifest, i.e., a value such that the polymer will have a molecular weight in the range of from about 5,000 to about 50,000, preferably a molecular weight in the range of from about 10,000 to about 35,000, more preferably a molecular weight in the range of from about 12,000 to about 25,000.

Termination of the living polymer by any of the above types of terminating agents is accomplished simply by adding the terminating agent to the solution of living polymer at the temperature at which the living polymer is prepared. Reaction is immediate and the yield is theoretical. A slight molar excess of the terminating agent, with respect to the amount of catalyst, may be used although the reaction proceeds on a molefor-mole basis.

The termination may be conducted in any suitable inert solvent. Generally, it is advisable to utilize the same solvent system employed in the preparation of the living polymer. A preferred embodiment of the invention comprises conducting the termination reaction in a hydrocarbon solvent rather than the polar ether type solvents such as tetrahydrofuran. It has been found that the hydrocarbon solvents such as the aromatic hydrocarbons, saturated aliphatic and cycloaliphatic hydrocarbons cause several differences in the reaction conditions and the resulting product. For example, the termination reaction can be conducted at higher temperatures with hydrocarbon solvents as opposed to the ether solvents.

sec-Bu EC -9, sec-BuE In some instances, because of the nature of the living polymer and the monomer from which it is prepared, or because of the nature of the terminating agent, certain deleterious side reactions occur which result in an impure product. For example, the carbanion of some living polymers have a tendency to react with functional groups or any active hydrogens of the terminating agent. Thus, for example, acrylyl or methacrylyl chloride while they act as terminating agents because of the presence of the chlorine atom in their structure, they also provide a carbonyl group in the terminated polymer chain, and this carbonyl group may provide a center for attack by a second highly reactive living sec-B polymer. The resulting polymer either has twice the expected molecular weight or contains some chlorine, indicating that some of the living polymer has been terminated by reaction with a second living polymer or with one of the active hydrocarbons of the acrylyl or methacrylyl chloride.

It has been discovered that one means for overcoming the foregoing problem is to render the reactive carbanion less susceptible to reaction with the functional groups or any active hydrogens of a terminating agent. A preferred method to render the living polymer less susceptible to the adverse reaction is to cap" the highly reactive living polymer with a lesser reactive reactant. Examples of some preferred capping agents include the lower alkylene oxides, i.e., one having eight or fewer carbon atoms such as ethylene and propylene oxide. The capping reaction yields a product which still is a living polymer, but yields a purer product when subsequently reacted with a terminating agent containing a functional group or active hydrogen.

A particularly preferred capping agent" is an alkylene oxide, such as ethylene oxide. It reacts with the living polymer, with the destruction of its oxirane ring. The following is a typical illustration of the capping reaction" which shows the reaction of ethylene oxide as a capping agent with a living polymer prepared by the polymerization of butadiene with sec-butyl lithium as the initiator:

The capping reaction is carried out quite simply, as in the case of the terminating reaction, by adding the capping reactant to the living polymer at polymerization temperatures. The reaction occurs immediately. As in the case of the termination reaction, a slight molar excess of the capping reactant with respect to the amount of initiator may be used. The reaction occurs on a mole-for-mole basis.

It will be understood that when a large molar excess of alkylene oxide is reacted with the living polymer, a living polymer having two polymeric blocks is produced. A typical example with polybutudiene segments and polyoxyalkylene segments is illustrated as follows:

wherein x is a positive integer.

Either of the above-described ethylene oxide capped polymers can be conveniently terminated with a compound containing a moiety reactive with the anion of the capped polymer and a polymerizable end group, such as acrylyl chloride or; methacrylyl chloride.

The reaction of the above-described capped living polymers with either acrylyl or methacrylyl chloride can be represented by the following reaction:

monomers must have nearly a Poisson molecular wherein n is a positive integer of about at least 50, x is either or a positive integer and R is either hydrogen or methyl.

As one embodiment of the invention, the terminated polymer containing an epoxy end group may be reacted with a polymerizable carboxylic acid halide, such as acrylic or methacrylic, halide, to produce a betahydroxyalkyl acrylate or methacrylate ester as the polymerizable terminal moiety of the substantially uniform molecular weight polymer. These same polymerizable esters may be prepared from the terminal epoxy polymer by first converting the epoxy group to the corresponding glycol by warming the polymer with aqueous sodium hydroxide, followed by conventional esterification of the glycol end group with the appropriate polymerizable carboxylic acid, or acid halide.

If it is desired to isolate and further purify the macromolecular monomer from the solvent from which it was prepared, any of the known techniques used by those skilled in the art in recovering polymeric materials may be used. These techniques include: (1) solvent-nonsolvent precipitation; (2) evaporation of solvent in an aqueous media; and (3) evaporation of solvent, such as by vacuum roll drying, spray drying, freeze drying; and (4) steam jet coagulation.

The isolation and recovery of the macromolecular monomer is not a critical feature of the invention. In fact, the macromolecular monomer need not be recovered at all. Stated otherwise, the macromolecular monomer, once formed, can be charged with the suitable monomer and polymerization catalyst to conduct the graft copolymerization in the same system as the macromolecular monomer was prepared, providing the solvent and materials in the macromolecular monomer preparation reactor do not poison the catalyst or act in a deleterious manner to the graft copolymerization process. Thus, a judicious selection of the solvent and purification of the reactor system in the preparation of the macromolecular monomer can ultimately result in a large savings in the production of the graft copolymers of the present invention.

As pointed out above, the macromolecular monomers, which ultimately become the sidechains of the graft copolymers by being integrally polymerized into the backbone polymer, must have a narrow molecular weight distribution. Methods for determining the molecular weight distribution of polymers such as the macromolecular monomers are known in the art. Using these known methods, the weight average molecular weight (191w) and the number average molecular weight (Mn) can be ascertained, and the molecular weight distribution (MW/Mn) for the macromolecular monomer can be determined. The macromolecular weight distribution or be virtually monodisperse in order to have the highest degree of functionality. Preferably, the ratio of lvlwllvln of the novel macromolecular monomers will be less than about 1.1. The macromolecular monomers of the present invention possess the aforementioned narrow molecular weight distribution and purity due to the method of their preparation, described hereinabove. Thus, it is important that the sequence of steps in preparing the macromolecular monomers be adhered to in order to produce the optimum results in beneficial properties in the graft copolymers.

GRAFT COPOLYMERIZATION Prior to the invention herein, graft copolymers were prepared by synthesizing a linear backbone", then grafting onto this backbone, growing polymeric or preformed polymeric chains. These methods generally require elaborate equipment and produce a mixture of products having inferior properties unless further purified. Because of the additional processing conditions and the use of special equipment, these processes are not economically feasible.

Although some of the prior art graft copolymers, such as those described in US. Pat. Nos. 3,627,837, 3,634,548 and 3,644,584 and British Pat. Nos. 873,656 and 1,144,151 resemble the graft copolymers of the present invention. Generally, the present graft copolymers are different compositions, not only because they are prepared by significantly different processes, but because the pendant polymeric chains of the graft copolymers of this invention are of relatively uniform, minimum length, and are each an integral part of the backbone. Furthermore, the backbone of the graft co- .polymers of the present invention contain polymeric segments of certain minimum length. Thus, the present graft copolymers differ structurally because the macromolecular monomer is interposed between polymeric segments of the backbone polymer, rather than being merely attached to the backbone polymer in a random manner. These characteristics contribute materially to the advantageous properties which inhere in these novel graft copolymers.

The graft copolymers of the present invention are prepared by first synthesizing the pendant polymeric chains (the polymerizable terminated living polymers) then copolymerizing the terminal portions of the polymeric chains with the second monomer during the formation of the backbone polymer.

In accordance with the practice of the present invention, the substantially pure macromolecular monomers of high controlled molecular weight and molecular weight distribution have an appropriate reactive end group suitable for any mechanism of-copolymerization, e.g., free-radical, cationic, anionic and Ziegler catalysis. Thus, the reactive end group is selected for easy copolymerization with low cost monomers by conventional means and within existing polymerization equipment.

The copolymerization with the macromolecular monomers and the second reactive monomer is a graftlike structure where the pendant chain is a polymer whose molecular weight and distribution are predetermined by independent synthesis. The distribution of the sidechain polymer along the backbone is controlled by the reactivity ratios of the comonomers.

Since the reactive end group of the macromolecular monomer is copolymerized with the second monomer, it is an integral part of the backbone polymer. Thus, the polymerizable end group of the macromolecular monomer is interposed between large segments of the backbone polymer.

The present invention provides a means for control ling the structure of the graft copolymer. More specfically, the control of the structure of the graft copolymer can be accomplished by any one or all of the fol lowing means: l by determining the reactivity ratio of the macromolecular monomer and a second monomer during the copolymerization reaction, a pure graft polymer free from contamination by homopolymers can be prepared; (2) by controlling the monomer addition rates during the copolymerization of a macromolecular monomer and a second monomer, the distance between the sidechains in the polymer structure can be controlled; and (3) the size of the graft chain can be predetermined and controlled in the anionic polymerization step of the preparation of the macromolecular monomer.

It will be apparent to those skilled in the art that by the proper selection of terminating agents, all mechanisms of copolymerization may be employed in preparing the controlled phase separated graft copolymers.

As alluded to hereinabove, the chemically joined, phase separated graft copolymers of the present invention are preferably copolymerized with any ethylenical ly-unsaturated monomer including the vinylidene type compounds containing at least one vinylidene group and preferably the vinyl-type compounds containing the characteristic CH CH group wherein hydrogen is attached to one of the free valences of the vinylidene group. The copolymerization,as pointed out above, is only dependent upon the relative reactivity ratios of the terminal group and the comonomer.

Examples of some of the preferred ethylenicallyunsaturated compounds used as the comonomers include the acrylic acids, their esters, amides and nitriles including acrylic acid, methacrylic acid, the alkyl esters of acrylic and methaerylic acid, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, N,N- dimethacrylamide (NNDMA); the vinyl halides such as vinyl chloride, and vinylidene chloride; the vinyl cyanides such as vinylidene cyanide (1,l-' dicyanoethylene); the vinyl esters of the fatty acids such as vinyl acetate, vinyl propionate and vinyl chloroacetate, etc.; and the vinylidene containing dicarboxylic anhydrides, acids and esters, fumaric acid and esters, maleic anhydrides, acids and esters thereof.

A particularly important class of vinylidene type compounds useful as comonomers with the alpha-olefin and styrene terminated macromolecular monomers include the vinyl olefinic hydrocarbons, such as ethylene, propylene, l-butene, isobutylene, l-pentene, l-hexene, styrene, 3-methyl-l-butene, 4-methyl-l-hexene and cyclohexene. Also, there may be used as the comonomers the polyolefinic materials containing at least one vinylidene group such as the butadiene-l .3-hydrocarbons including butadiene, isoprene, piperylene and other conjugated dienes, as well as other conjugated and nonconjugated polyolefinic monomers including divinyl benzene, the diacrylate type esters of methylene, ethylene, polyethylene glycols, and polyallyl sucrose.

The most preferred ethylenically unsaturated comonomers are the commercially available and widely used monomers such as methyl acrylate, butyl acrylate, 2- ethyl hexyl acrylate, ethyl methacrylate, vinyl chloride, vinylidene chloride, vinylidene cyanide, acrylonitrile; and the hydrocarbon monomers such as ethylene, propylene, styrene; and the conjugated dienes such as butadiene and isoprene.

The placement of the sidechain in the polymer backbone is dependent on the terminal group of the macromolecular monomer and the reactivity of the comonomer.

The macromolecular monomers of the invention are stable in storage and do not significantly homopolymerize. Furthermore, the macromolecular monomer copolymerizes through the terminal double bond or reactive end group and is not incorporated into the polymeric backbone by grafting reactions to the polymer of the macromolecular monomer segment.

As indicated hereinabove, the macromolecular monomers of the invention copolymerize with commercial vinyl monomers in a predictable manner as determined by relative reactivity ratios. It can be shown that the instantaneous copolymer equation:

simply reduces to the approximation:

(2) dM,/dM M /r M when M is in very low molar concentrations. Thus, the macromolecular monomer (M copolymerizations with other monomers (M are described only by r values and monomer feed compositions. Rearrangement of equation (2) gives:

(3) r (dM /M )/(dM,/M Conversion M Conversion M The reactivity ratio, r can be estimated from a relatively low conversion sample of a single copolymerization experiment. The validity of this concept of a predictable and controllable reactivity of the macromolecular monomer can thereby be established. It has been shown that the reactivity of commercial mono mers with the macromolecular monomers of the present invention with various end groups correlate with available literature values for reactivity ratios of r The method of the present invention permits the utilization of all types of polymerizable monomers for incorporation into backbone polymers, and makes it possible for the first time to design and build graft copolymers of controlled molecular structure, and of backbone and graft segments'with different properties, such as hydrophobic and hydrophilic segments, crystalline and amorphous segments, polar and non-polar segments, segments with widely different glass transition temperatures, whereas prior work on SDS terblock copolymers had been limited to the incompatibility of glass polystyrene blocks with rubbery polydiene blocks.

The copolymerization of the polymerizable macromolecular monomers with the comonomers may be conducted in a wide range of proportions. Generally speaking, a sufficient amount of the macromolecular monomer should be present to provide the chemically joining of at least one of the uniform molecular weight sidechain polymers to each backbone polymer, so that a noticeable effect on the properties of the graft copolymeric properties can be obtained. Since the molecular weight of the polymerizable macromolecular monomer generally exceeds that of the polymerizable comonomers, a relatively small amount of the polymerizable macromolecular monomer can be employed. However, the chemically joined, phase separated thermoplastic graft copolymers may be prepared by copolymerizing a mixture containing up to about 95% by weight, or more, of the polymerizable macromolecular monomers of this invention, although mixtures containing up to about 60% by weight of the polymerizable macromolecular monomer are preferred. Stated otherwise, the resinous thermoplastic chemically joined, phase separated graft copolymer of the invention is comprised of (l) from 1 to about 95% by weight of the polymerizable macromolecular monomer having a narrow molecular weight distribution (i.e., a Mw/Mn of less than about 1.1), and (2) from 99 to about 5% by weight of a copolymerizable comonomer defined hereinabove.

The polymerizable macromolecular monomers copolymerize with the hereinabove referred to comonomers in bulk, in solution, in aqueous suspension and in'aqueous emulsion systems suitable for the particular polymerizable macromolecular monomer, its end group and the copolymer employed. If a catalyst is employed, the polymerization environment suitable for the catalyst should be employed. For example oilor solventsoluble peroxides such as benzoyl peroxides, are generally effective when the polymerizable macromolecular monomer is copolymerized with an ethylenically unsaturated comonomer in bulk, in solution in an organic solvent such as benzene, cyclohexane, toluene, xylene, etc., or in aqueous suspension. Water-soluble peroxides such as sodium, potassium, lithium and ammonium persulfates, etc. are useful in aqueous suspension and emulsion systems. In the copolymerization of many of the polymerizable macromolecular monomers, such as those with the ethylenically unsaturated end group and the polyisoprene or polybutadiene repeating unit, an

emulsifier or dispersing agent may be employed in aqueous suspension systems. In these systems, particular advantage can be achieved by dissolving the waterinsoluble polymerizable macromolecular monomer in a small amount of a suitable solvent, such as a hydrocarbon. By this novel technique, the comonomer copolymerizes with the polymerizable macromolecular monomer in the solvent, in an aqueous system surrounding the solvent-polymer system. Of course, the polymerization catalyst is chosen such that it will be soluble in the organic phase of the polymeriation system.

As previously stated, various different catalyst systems can be employed in the present invention for the copolymerization process. It will be apparent to those skilled in the art that the particular catalyst system used in the copolymerization will vary, depending on the monomer feed and the particular end group on the macromolecular monomer. Since the particular polymerizable end group on the macromolecular monomer will depend on the comonomer feed employed because of the relative reactivity ratios, the polymerization mechanism commonly employed for the particular comonomer will be used. For example, ethylene polymerizes under free-radical, cationic and coordination polymerization conditions; propylene and higher alphaolefins only polymerize under coordination polymerization conditions; isobutylene only polymerizes under cationic polymerization conditions; the dienes polymerize by free-radical anionic and coordination polymerization conditions; styrene polymerizes under freeradical, cationic, anionic and coordination conditions; vinyl chloride polymerizes under free-radical and coordination polymerization conditions; vinylidene chloride polymerizes under free-radical polymerization conditions; vinyl fluoride polymerizes under free-radical conditions; tetrafluoroethylene polymerizes under freeradical and coordination polymerization conditions; vinyl ethers polymerize under cationic and coordination polymerization conditions; vinyl esters polymerize under free-radical polymerization conditions; acrylic and methacrylic esters polymerize under free-radical, anionic and coordination polymerization conditions; and acrylonitrile polymerizes under free-radical, anionic and coordination polymerization conditions.

It will be understood by those skilled in the art that the solvent, reaction conditions and feed rate will be partially dependent upon the type of catalyst system utilized in the copolymerization process. One of the considerations, of course, will be that the macromolecular monomer be dissolved in the solvent system utlized. it is not necessary, however, for the monomer feed to be soluble in the solvent system. Generally, under these conditions during the formation of the copolymer, the graft copolymer will precipitate out of the solvent wherein it can be recovered by techniques known in the polymer art.

The temperature and pressure conditions during the copolymerization process will vary according to the type of catalyst system utilized. Thus, in the production of low density polyolefin backbones under free-radical conditions, extremely high pressures will be employed. On the other hand, the high density substantially linear polyolefin backbone polymers produced by the coordination type catalyst generally will be prepared under moderately low pressures.

When preparing graft copolymers having a polyolefin backbone of ethylene or propylene or copolymers of ethylene and propylene together with a macromolecular monomer, it is preferred to employ a coordination catalyst known in the art as the Ziegler catalyst and Natta catalysts (the latter being commonly used for polypropylene). That is, materials advanced by Professor-Dr. Karl Ziegler of the Max Planck Institute of Mulheim, Ruhr, Germany, and Dr. Giulio Natta of Milan, Italy. Some of these catalysts are disclosed in Belgian Pat. No. 533,362, issued May 16, 1955, and U8. Pat. Nos. 3,113,115 and 3,257,332 to Ziegler et al. These catalysts are prepared by the interaction of a compound of transition metals of group lV-Vlll in the periodic table, the catalyst, and an organo-metallic compound derived from group [-111 metals, as co-catalyst. The latter are compounds such as metal hydrides and alkyls capable of giving rise to hydride ions or carbanions, such as trialkyl aluminum. Compounds of the transition elements have a structure with incomplete d-shells and in the lower valance states, can associate with the metal alkyls to form complexes with highly polarized bonds. Those elements hereinabove referred to as the catalysts are preferably titanium, chromium, vanadium, and zirconium. They yield the best Ziegler catalysts by reaction of their compounds with metal alkyls.

As previously stated, the solvent system utilized will most conveniently be the solvent employed in the preparation of the macromolecular monomer.

The copolymerization reaction may be conducted at any suitable temperature, depending on the particular catalyst, macromolecular monomer, monomer feed, resulting graft copolymer and solvent used. Generally, the graft copolymerization will be conducted at a temperature of from about C to about 500C, preferably from about 20C to about 100C.

The graft copolymerization reaction is preferably conducted by placing a predetermined amount of the macromolecular monomer dissolved in the appropriate solvent in the reactor The polymerization catalyst and monomer are thereafter fed into the solvent system to produce the graft copolymer.

It is generally desirable to'provide a graft copolymer having at least about 2% macromolecular monomer incorporated in the backbone polymeric material, however, satisfactory results can be obtained with up to about 40% by weight macromolecular monomer incorporation. Preferably, the graft copolymers of the present invention will have about 5 to about 20% by weight incorporation of the macromolecular monomer into the backbone polymeric material to obtain the optimum physical properties of both the sidechain polymer and the backbone polymer. However, graft copolymers having up to about 95% by weight of the macromolecular monomers incorporated therein may be prepared and are contemplated within the scope of the inventron.

The means for providing the proper amount of incorporation of the macromolecular monomer can be determined simply by adding the appropriate weight macromolecular monomer used in the copolymerization process. For example, if a graft copolymer having 10% by weight incorporation of the macromolecular monomer into the backbone polymer is desired, one simply employs 10 parts by weight of the macromolecular monomer for each 90 parts by weight of the monomer feed.

Following the procedures outlined above, graft copolymers having unique combinations of properties are produced. These unique combinations of properties are made possible by thenovel process herein which forces the compatibility of otherwise incompatible polymeric segments. These incompatible segments segregate into phases of their own kind. 7

The chemically joined, phase separated graft copolymers of the invention microscopically possess a controlled dispersion of the macromolecular sidechain in one phase (domain) within the backbone polymer phase (matrix). Because all of the macromolecular monomer sidechain domains are an integral part or interposed between large segments of the backbone polymer, the resulting graft copolymer will have the properties of a cross-linked polymer, if there is a large difference in the Tg or Tm of the backbone and sidechain segments. This is true only up to the temperature required to break the thermodynamic cross-link of the dispersed phase. In essence, a physically cross-linked (as opposed to chemical cross-linked) type polymer can be made that is reprocessable and whose properties are establilshed by simple cooling,-rather than vulcanization or chemical cross-linking.

The graft copolymers of the present invention are differentiated from the macroscropic opaque and weak blends of incompatible polymers of the prior art. The graft copolymers of this invention contain separate phases which are chemically joined and the dispersion of one segment into the matrix polymer is on a microscopic level and below the wavelength of light of the matrix polymer. The graft copolymers herein are, therefore, transparent, tough, and truly thermoplastic.

The uninterrupted polymeric segments of the backbone of such a graft copolymer will be polymeric segments of ethylene and propylene.

The graft copolymers comprising polymeric segments having fewer than about 20 recurring monomeric units are, nevertheless, useful for many applications, but the preferred graft copolymers are those in which the various polymeric segments have at least about 20 recurring monomeric units.

Although, as indicated, the graft copolymers herein are characterized by a wide variety of physical properties, depending on the particular monomers used in their preparation, and also on the molecular weights of the various polymer segments within a particular graft copolymer, all of these graft polymers are useful, as tough, flexible, self-supporting films. These films may be used as food-wrapping material, painters dropcloths, protective wrapping for merchandise displayed for sale, and the like.

Graft copolymers of the macromolecular monomer, polystyrene, with ethylene-propylene, isobutylene, or propylene oxide monomers have been found to be stable materials that behave like vulcanized rubbers, but are thermoplastic and reprocessable. Thus, an extremely tough, rubbery plastic is obtained without the inherent disadvantages of a vulcanized rubber. These copolymerized rubber-forming monomers with the macromolecular monomers of the present invention have the additional use as an alloying agent for dispersing additional rubber for impact plastics.

Just as metal properties are improved by alloying, so are polymer properties. By adding the appropriate amount of an incompatible material to a plastic in a microdispersed phase, over-all polymer properties are improved. A small amount of incompatible polybutadiene rubber correctly dispersed in polystyrene gives high impact polystyrene. The key to this microdispersion'is a small amount of chemical graft copolymer that acts as a flux for incorporating the incompatible rubber.

A copolymer of the macromolecular monomer of the present invention can be the fluxfor incorporating or dispersing incompatible polymers into new matrices making possible a whole new line of alloys, impact plastics, malleable plastics and, easy-to-process plastics.

The reinforcement of plastics by adding glass fibers or other materials is difficult to achieve because of ing in any respect. ln each case, all materials should be pure and care should be taken to keep the reactedmixtures dry and free of contaminantsall parts and percentages, unless expressly stated to be otherwise, are by weight.

EXAMPLE 1 a. Preparation Of Polystyrene Terminated With Methacrylyl Chloride:

To a solution of 0.2 ml. of diphenyl ethylene in 2500 ml. of benzene there is added dropwise a 12% solution of 'n-butyl lithium in hexane until the persistence of a light reddish-brown color. An additional 24 ml. (0.031 mole) of this n-butyl lithium solution'is added, and then, 416 grams (4.0 moles) of styrene, resulting in the development of an orange colorgA temperature of 40C is maintained throughout by external cooling and by controlling the rate at which the styrene is added. This temperature is maintained for an additional 30 minutes after all of the styrene has been added, and

polyisoprene. The low T, living polymer is terminated by the addition of a molar equivalent, based on sec- V butyl lithium, ethylene oxide as a capping agent, followed by a molar equivalent amount of allyl chloride to produce a polymer predominantly having the following structural formula:

EXAMPLE 2 Preparation Of Polystyrene Terminated With Methacrylyl Chloride A stainless steel reactor is charged with 32 gallonsof A.C.S. grade benzene (thiophene-free), which had been predried by Linde molecular sieves and calcium hydride. The reactor is heated to a temperature of between 38-40C and 10 ml. of diphenyl ethylene is added to the reactor by means of a hypodermic syringe. An 1 1.4% solution of secondary butyl lithium in hexane is added to the reactor portionwise until the retention of a permanent orange-yellow color is obtained (60 then is lowered to 20C, whereupon 4.4 grams (0.1

mole) of ethylene oxide is added, causing the solution to become colorless. The living polymer is terminated by rection with 10 ml. (0.1 mole) of methacrylyl chloride. The resulting polymer has a number average molecular weight as shown by vapor phase osmometry of 10,000. The macromolecular monomer has the following structural formula:

v u ca cu occ cs ml.), at which point an additional 3.44 pounds of the secondary butyl lithium in hexane is added to the reactor, followed by the addition of 82.5 pounds of purified styrene over a period of 1 hour and 40 minutes. The reactor temperature is maintained at 3840C. The living polystyrene is capped by the addition of 0.28 pounds of ethylene oxide and the reaction solution changes from a red-orange color to yellow. The resulting capped living polystyrene is thereafter reacted with 260 ml. of methacrylyl chloride and the solution changes to a very pale yellow color. The methacrylate terminated polystyrene is precipitated by the addition of the polymer benzene solution into methanol, whereuponthe polymer precipitates out of solution. The polymer is dried in an air circulating atmosphere drier at 4045C and then in a fluidized bed toremove the trace amounts of methanol. The molecular weight of the polymer as determined by membrane phase osmometry, is 13,400

and the molecular weight distribution is very narrow,

i.e.,the Mw/K ln is less than 1.05.

EXAMPLE 3 densed and collected in l-pint soda bottles. These bote. Maleic anhydride is substituted for methacrylyl chloride in procedure (a), followed by protonation with water to produce polystyrene terminated with the half ester of maleic acid.

f. Epichlorohydrin is substituted for methacrylyl chloride to produce an epoxy etherterminated polystyrene.

g. The procedure of (a) is repeated using in place of styrene, an equivalent amount of isoprene and in place of n-butyl lithium an equivalent amount of sec-butyl lithium to produce primarily a rubbery sis-1,4-

tles had been oven baked for 4 hours at C, nitrogen purged during cooling, and capped with a perforated metal crown cap using butyl rubber and polyethylene film liners. These bottles containingthe butadiene are stored at l0C with anitrogen pressure head (10 psi) in a laboratory freezer before use. Hexane solvent is charged to the reactors and heated to 50C, followed by the addition of 0.2 ml. of diphenyl ethylene by way of a syringe. Secondary butyl lithium is added dropwise via syringe to the reactor until the red diphenyl ethylene anion color persists for at least about 10-15 minutes. The reactor temperature is lowered to0C, and

- (0.02187 mole of a 12% secondary butyl lithium solution is hexane, when half of the butadiene charge has been added to the reactor. The butadiene is polymerized for 18 hours in hexane at 50C,. Following the polymerization, 400 ml. portions of the anionic polybutadiene solution in the reactor is transferred under nitrogen pressure into capped bottles. Allyl chloride (0.48 ml., 0.00588 mole) is injected into each of the bottles. The bottles are clamped in water baths at temperatures of 50C and 70C for periods of time ranging up to 24 hours. The samples in each of the bottles are short stopped with methanol and lonol solution and analyzed by Gel Permeation Chromatography. Each of the samples is water white and the analysis of the Gel Permeation Chromatography scans reveals that each of the samples had a narrow molecular weight distribution.

Several comparison samples were conducted in bottles coming from the same lot of living polybutadiene, which were capped with 2-chlorobutane (0.4 ml., 0.00376 mole) as the terminating agent. The resulting polymers terminated with 2-chlorobutane were yellow in color and after standing for a period of 24 hours at 70C, appeared to have a broad molecular weight distribution as revealed by the Gel Permeation Chromatography scan. It is clear that the reaction and reaction product of 2-chlorobutane with anionic polybutadiene are different than the reaction and reaction product of allyl chloride and anionic polybutadiene.

EXAMPLE 4 Preparation Of Methaerylate Terminated Polyisoprene ate terminated polyisoprene by Gel Permeation Chromatography was about 10,000 (theory: 13,000). The methacry-late terminated polyisoprene macromolecular monomer had a structural formula represented as follows:

ll H /C 2 CHZCHZOC C CH C I C CH 3 CH H n EXAMPLE 5 Preparation of Alpha-Olefin Terminated Polyisoprene A one-gallon Chemco glass-bowl reactor is charged with 2.5 liters of purified heptane which had been predried by a Linde molecular sieve and calcium hydride, followed by the addition of 0.2 ml. of diphenyl ethylene as an indicator. The reactor and solvent are sterilized by the dropwise addition of tertiary butyl lithium solu' tion (12% in hexane) until the retention of the characteristic light yellow color is obtained. The reactor is heated to 40C and 19.03 ml. (0.02426 mole) of ter tiary butyl lithium solution is injected into the reactor via hypodermic syringe, followed by the addition of 315.5 grams (4.63 moles) ofisoprene. The polymerization is permited to proceed at C for 66 minutes and at this time 2.0 ml (0.02451 mole) of allyl chloride is added to the living polyisoprene. The terminated polyisoprene is held at 50C for 38 minutes, whereupon the polymer is removed from the reactor to be used in copolymerization reactions. The polymer was analyzed by Gel Permeation Chromatography and had a very narrow molecular weight distribution, i.e., an Mw/lTin of less than about 1.06. The theoretical molecular weight ofthe polymer is 13,000. The polymerizable macromolecular monomer had a structural formula represented A one-gallon Chemco glass-bowl reactor is charged 40 as follows:

with 2.5 liters of purified heptane which had been predried by a Linde molecular sieve and calcium hydride, followed by the addition of 0.2 m1. of diphenyl ethylene as an indicator and the reactor is sterilized with the dropwise addition of tertiary butyl lithium solution (12% in hexane) until the retention of the characteristic light yellow color is obtained. The reactor is heated to 40C and 19.9 ml. (0.025 mole) of a 12% solutionof tertiary butyl lithium in hexane is injected into the reactor via hypodermic syringe, followed by the addition of 331.4 grams (4.86 moles) of isoprene. The mixture is allowed to stand for one hour at 40C and 0.13 mole of ethylene oxide is charged into the reactor to cap the living polyisoprene. The capped living polyisoprene is held at 40C for 40 minutes, whereupon 0.041 mole of methacrylyl chloride is charged into the. reactor to terminate the capped living polymer. The mixture is held for 13 minutes at 40C, followed by removal of the heptane solvent by vacuum stripping. Based upon the Gel Permeation Chromatography scans for polystyrene, the molecular weight of the methacryl- CH C CHCH=CH;

CH H n Sidechain polymers having a high Tg, such as polystyrene can be replaced with low Tg polymers such as polybutadiene and predominantly cis-polyisoprene. For example, isoprene can be anionically polymerized with secondary butyl lithium, preferably to a molecular weight of about 15,000 and terminated with allyl chloride. Alternatively, the rubbery living polymer can be capped with an alkylene oxide such as ethylene oxide followed by termination with allyl chloride, methallyl chloride, or methacrylyl chloride to obtain low Tg macromolecular monomers. The alpha-olefin terminated (allyl chloride and anionically polymerized isoprene) can be used to prepare super impact polyethylene or polypropylene copolymers utilizing known polymerization techniques. For example, the alpha-olefin terminated polyisoprene referred to above can be copolymerized with ethylene using a Ziegler type catalyst system or with propylene using a Natta type catalyst system.

The present invention provides a convenient and economical means for preparing copolymers utilizing a large variety of hydrocarbon monomers in forming the backbonepolymeric blocks and a wide variety of anionically polymerizable monomers in forming the sidechain polymers. The copolymerization is facilitated by a judicious selection of the terminal end group on the anionically polymerized polymer. Thus, the problem of copolymerizing incompatible polymers is solved providing an economical means for preparing copolymers having a backbone and sidechain polymer designed to fit ones needs and the particular end product desired. The macromolecular monomers of the invention copolymerize with acrylates and other polymerizable monomers throughthe terminal double bond.

EXAMPLE 6 Preparation Of Graft Copolymer Having Polyisoprene Sidechains And Polystyrene Backbone A 370 gram charge of the 7.1% methacrylate terminated polyisoprene macromolecular monomer prepared in Example 4 is vacuum stripped 1% hours at 50C on a rotary evaporator (6.1 grams of heptane is not removed by stripping). The round bottomed flask containing the concentrated macromolecular monomer is sealed with a septum and purged with nitrogen. A solution consisting of 61.2 grams of styrene, 6.1 grams benzene (thiophene-free) and 0.31 gram of AlBN (0.5% by weight styrene) is introduced by syringe and the macromolecular monomer is allowed to dissolve. The clear monomer solution is transferred by syringe into a well-purged 12 ounce bottle containing a aqueous polyvinyl pyrrolidone-solution (300 grams of water, 0.24 gram Luviskol K-90 (PVP, 0.3% by weight)). The bottle is capped, briefly purged with nitrogen, and rotated in a 65C bottle polymerization bath. After 17.5 hours at 65C, the bottle is finished at 95C for 3 hours.

The product beads are filtered on a screen, washed with distilled water, and dried at 40C under vacuum. The product is milled for 2 minutes at 150C and 0.40 gram Ionol CP antioxidant is added on the mill. A yield of 75.8 grams of transparent milled product is obtained. The styrene conversion is 98%.

Polyblends Employing Macromolecular Monomers As Alloying Agents Polyvinyl chloride blends with low levels of the macromolecular monomer/polyacrylate graft copolymers of the invention provide products that are clear, have improved processing and high impact properties. Notched lzod impact strengths of 22 ft. lbs/inch are obtained with little loss in flexural modulus in rigid polyvinyl chloride blends containing as little as 3% of the macromolecular monomer/poly(butyl acrylate) graft copolymer. The graft copolymers of the invention also function as processing aids by improving polyvinyl chloride fusion in milling and compression molding. The graft copolymers also impart high strength to higher molecular weight polyvinyl chloride polymers,

such as Vygen 110 and 120, when low levels of the graft copolymer (macromolecular monomerpoly(butyl acrylate) is blended after the polyvinyl chloride is banded on the mill.

The polyvinyl chloride polyblends with the graft copolymers have exceptionally high impact strength and are useful in pipe, siding, downspouts, cases, etc. This is unexpected because polyvinyl chloride is known for its low impact strength. Po1y(methyl methacrylate) also has low impact strength, however, when methyl methacrylate is either blended or copolymerized with the lower Tg or rubbery macromolecular monomers of the invention, the impact strength is enhanced.

Examples of polymers which can be blended with the graft copolymers of the invention to improve the melt rheology include polymers of vinyl chloride, methyl methacrylate, acrylonitrile, and others.

While the invention has been described in connection with specific embodiments thereof, it will be understood that it is capable of further modification, and this application is intended to cover any variations, uses, or adaptations of the invention following, in general, the principles of the invention and including such departures from the present disclosure as come within known or customary practice in the art to which the invention pertains and as may be applied to the essential features hereinbefore set forth, and as fall within the scope of the invention.

We claim:

1. A copolymerizable macromolecular monomer having a substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not substantially above about 1.1, wherein Mw is the weight average 20. weight of the macromolecular monomer, and Mn is the number average molecular weight of the macromolecular monomer, said macromolecular monomer being represented by the structural formula:

wherein R is loweralkyl and R and R" are each either hydrogen or methyl, and n is a positive integer having a value of at least about 20.

2. The copolymerizable macromolecular monomer of claim. 1, wherein R and R" are each methyl.

3. The copolymerizable macromolecular monomer of claim 1, wherein R is represented by the structural formula CH CH (CH )CH.

4. The copolymerizable macromolecular monomer of claim 1, wherein'n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 5,000 to 50,000.

5. The copolymerizable macromolecular monomer of claim 1, wherein n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 10,000 to about 35,000.

6. The copolymerizable macromolecular monomer of claim 1, wherein n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 12,000 to about 25,000.

7. The copolymerizable macromolecular monomer of claim 1, wherein Rand R" are each hydrogen.

8. A copolymerizable macromolecular monomer having a substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not substantially above about 1.1, wherein Mw is the weight average molecular weight of the macromolecular monomer, and Mn is the number average molecular weight of the macromolecular monomer, said macromolecular monomer being represented by the structural formula:

wherein 'n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 5,000 to about 50,000.

9. The copolymerizable macromolecular monomer of claim 8, wherein n has a value such that the molecular weight of the macromolecular monomer is in the 

2. The copolymerizable macromolecular monomer of claim 1, wherein R'' and R'''' are each methyl.
 3. The copolymerizable macromolecular monomer of claim 1, wherein R is represented by the structural formula CH3CH2(CH3)CH-.
 4. The copolymerizable macromolecular monomer of claim 1, wherein n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 5,000 to 50,
 000. 5. The copolymerizable macromolecular monomer of claim 1, wherein n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 10,000 to about 35,000.
 6. The copolymerizable macromolecular monomer of claim 1, wherein n is a value such that the molecular weight of the macromolecular monomer is in the range of from about 12,000 to about 25,000.
 7. The copolymerizable macromolecular monomer of claim 1, wherein R''and R'''' are each hydrogen.
 8. A copolymerizable macromolecular monomer hAving a substantially uniform molecular weight distribution such that its ratio of Mw/Mn is not substantially above about 1.1, wherein Mw is the weight average molecular weight of the macromolecular monomer, and Mn is the number average molecular weight of the macromolecular monomer, said macromolecular monomer being represented by the structural formula:
 9. The copolymerizable macromolecular monomer of claim 8, wherein n has a value such that the molecular weight of the macromolecular monomer is in the range of from about 10,000 to about 35,000.
 10. The copolymerizable macromolecular monomer of claim 8, wherein n has a value such that the molecular weight of the macromolecular monomer is in the range of from about 12,000 to about 25,000. 